Sinter is the primary feed material for making iron in a blast furnace. During the iron ore sintering process in iron and steel manufacturing, sinter is created by mixing iron ore concentrate with several additives such as limestone and silica to control the chemistry and then igniting it at 1200°C in a continuous beltfed furnace. The production of highquality sinter is crucial for assuring ...
Sinter plants agglomerate iron ore fines (dust) with other fine materials at high temperature, to create a product that can be used in a blast final product, a sinter, is a small, irregular nodule of iron mixed with small amounts of other minerals. The process, called sintering, causes the constituent materials to fuse to make a single porous mass with little change in the chemical ...
problems in the sintering process as well as inthe blastfurnace ironmaking. 1 It is widely known that alkali metals like potassium and sodium cause operational problems in the iron blast furnace ...
shows the iron ore blend mix proportion and mean particle size (MPS) for the iron ore blend for all the experiments. The high Fe and low LOI concentrate within the pellet nes compared to other iron ores can act as a suitable feed for the sinter making process. The amount of micro nes (− 150 µm) in pellet nes is % which is quite high
2 Raw Materials. Impure iron is produced from reduction of iron ore by means of coke in a blast furnace. The product is a liquid iron, known as hot metal (% C, % Si, % Mn, etc.) which is raw material for production of steel. Hot metal is refined by oxidation process to form steel.
The sintering process produces iron ore agglomeration of size 1040 mm with better reducibility values than lumps. Utilization of a higher proportion of quality agglomerates in the burden increases the productivity of the blast furnace. The sintering process increases the productivity and reduces the requirement of fuel, flux, and operation time.
Due to the fierce competition among iron and steel industries, improvement in sinter quality has already become a hot topic in ironmaking process. Sinter ore with superior strength and reducibility promotes the smooth running of blast furnace and decreases the consumption of fuel [, ]. Complex calcium ferrite, which also named silicoferrite of ...
During the iron ore sintering process trace elements can have four different destinations: remain in the sinter product, be retained by the abatement methods in the form of particulates, be emitted into the atmosphere as particulate material, or be emitted into the atmosphere in the gaseous form ( Xu et al., 2004 ).
Impact of Biopellet on Sintering Temperature Profiles. Figure 3 shows the temperature profile observed during iron ore sintering process at different proportions of biopellet. With an increase in biopellet the maximum temperature within the sinter bed reduces. In the presence of biomass, the water content required to granulate the sinter raw mix to a moisture levels of 8% increased from 8 ...
During the iron ore sintering process, its SiO2 content considerably affects the sinter quality. In this study, the effect of SiO2 content on iron ore sintering indexes was studied, with mineral composition and microstructure analyses. It was shown that the strength and reducibility of sintering products improved when SiO2 content increased.
Ore Sintering. The aim of the MEBIOS process is the formation of a ventilation route in the sintering bed by creating a lowdensity area around the large pellets arising from a kind of wall effect and suppression of sinter bed shrinkage due to support of the load by the dense large pellets in the upper part of the sinter bed. From: Iron Ore, 2015.
Meanwhile, an iron ore sinter is a crucial material for the ironmaking process, and its chemical, physical, and metallurgical properties significantly impact the blast furnace (BF) performance. 9 In turn, the main materials used for a sinter are iron ore fines, and their chemical compositions play a critical role in the sintering process.
Meanwhile, an iron ore sinter is a crucial material for the ironmaking process, and its chemical, physical, and metallurgical properties significantly impact the blast furnace (BF) performance. In turn, the main materials used for a sinter are iron ore fines, and their chemical compositions play a critical role in the sintering process. Due to ...
Sinter making is an agglomeration process of iron ore fines. As sizes of iron ore fines are very small, iron ores are converted into sinter before charging to Blast furnace. Quality of the sinter depends on different parameters namely raw material, gas flow, heat pattern in sinter bed and granulation of sintering.
1. Introduction. Iron ore sintering is an important hot agglomeration preprocess for ironmaking in most integrated steel mills. This process converts a mixture of ore fines, fluxes, return fines and plant dust to sinter by partial melting and resolidification of the granulated particles in a moving grate, in which the coke breeze is typically used as solid fuel with mixing ratios of 35 wt ...
In this article, the feasibility of this process was estimated from the point of the effects of MSWI fly ash addition on the iron ore sintering process, sinter mineral phase structure and ...
Sintering process is a generic term that is used to describe the process of agglomeration of a green mix of iron ores, fluxes and coke and plant solid wastes having a particle size of 10 mm so as to produce sinter which can withstand operating pressure and temperature conditions existing in a BF.
The sintering raw materials used in this test were from a Chinese iron and steel enterprise, including blended ore, return ore, dolomite, quicklime, coke, outsourced coke, fly ash, etc. The orematching scheme of the sintering pot test is shown in Table 4. In the test, dolomite was used as MgObearing flux, the proportion was fixed, and the ...
Like other sintering processes, iron ore sintering converts iron ore fines of often − 8 mm sizing into larger agglomerates, namely, sinter, between 5 and 50 mm particle size, which possess the physical and metallurgical characteristics and gas permeability required for efficient blast furnace operation.
Section snippets Experimental method and parameters quantification. The commercial tests in sintering grate are enormously expensive. If the transfer phenomena in the directions of grate length and width are neglected, iron ore sintering can be considered as 1D (in the direction of bed height) unsteady process.
The coke combustion rate in an iron ore sintering process is one of the most important determining factors of quality and productivity. Biomass carbon material is considered to be a coke substitute with a lower CO2 emission in the sintering process. The purpose of this study was to investigate the combustion rate of a biomass carbon material and to use a sintering simulation model to calculate ...
Iron making. The primary objective of iron making is to release iron from chemical combination with oxygen, and, since the blast furnace is much the most efficient process, it receives the most attention here. Alternative methods known as direct reduction are used in over a score of countries, but less than 5 percent of iron is made this way.
In the modern high basicity iron ore sintermaking process, complex calcium ferrites consisting of predominantly Fe, Ca, Al, Si, (Mg) and O are formed from high temperature reactions between the iron ore fines, coke breeze and flux ().The calcium ferrite phases are considered the dominant bonding phases in the sinter product and are usually grouped together under the acronym 'SFCA' (Silico ...
Lowtemperature (< 1300 °C) iron ore sinter is an agglomerate of unmelted and partially melted nuclei particles (+ 1 mm) and a matrix bonding phase produced from the melting of fine ore (− 1 mm) and flux particles, with the majority of melt formation occurring in the granule adhering fines layer.
Moreover, the conventional iron making unit, blast furnace requires the raw material in the form of iron oxide with a size range of 10120 mm. Sintering is the oldest agglomerate thermal process using iron ore mineral fines of mm, along with the reductant, fluxes, and other byproducts of the iron and steel industry operated ...
The process of sintering is basically a pretreatment process step during iron making for the production of the charge material called sinter for the blast furnace from iron ore fines and also from metallurgical wastes (collected dusts, sludge and mill scale etc.).
1 Introduction The sinter mix contains various materials such as iron ore, flux, solid fuel, plant return sinter fines, plant generated wastes, etc., where the majority of it is iron ore.
Sintering is a thermal agglomeration process that is applied to a mixture of iron ore fines, recycled ironmaking products, fluxes, slagforming agents, and solid fuel (coke). The purpose of the sintering process is manufacturing a product with the suitable characteristics (thermal, mechanical, physical and chemical) to be fed to the blast furnace.
The nontarget volatile organic compounds (VOCs) emissions from iron and steel industry, especially from the iron ore sinter process, may be an underappreciated index imposing a negative effect on the surrounding areas of China. Therefore, we appeal the authorities to pay more attention on VOCs emission from the iron and steel industry and ...